Datasheet - Pump Mirror 101544

[  ~  ]
List all articles with the similar coating
Print
Pump Mirror:
Fused silica | pl-concave | Ø=12.7(-0.1)mm | te=6.35(±0.10)mm | //<5min
S1: Øe8 | 3/0.2(0.2) [L/10] | 5/1x0.025; L1x0.004 | chamfer 0.3
     ARu(10°,500-700nm)<0.8%
S2(^): r=150mm(±0.5%) CC | Øe8 | 3/-(0.2) [L/10 reg.] | 5/1x0.025;
L1x0.004 | chamfer 0.3
     HRu(10°,1030-1360nm)>99.8% + Ru(10°,530-630nm)<5%

Product

concave+plane
Round
Article
101544
Type
  • Pump Mirror
Laser category
  • cw-Laser Optics
  • ns-Laser Optics
Laser type
  • Yb:YAG-Laser
  • Nd:YAG-Laser
Coating material (front side)
113621
Coating material (rear side)
120998
Price per unit (net.)
$183.97
discount ▼
from 5 pieces
5 %
from 10 pieces
10 %
from 20 pieces
20 %
Stock
0

General Optical Parameters

Material
Fused Silica
Shape
Round
Diameter (Ø)
12.7 mm
(-0.1  mm)
Thickness (t)
6.35 mm
(±0.1 mm)
Parallelism

Optical Parameters Front Side  (S2)

Optical Parameters Rear Side  (S1)

Shape
concave
Radius of curvature
150 mm
(±0.5 %)
Chamfer
0.3 mm
(±0.1 mm)
Test area Øe
10
Surface form tolerance
3/-(0.2) [L/10 reg. @546.1nm]
Cleanliness
5/1x0.025; L1x0.004
Shape
plane
Chamfer
0.3 mm
(±0.1 mm)
Test area Øe
10
Surface form tolerance
3/0.2
Cleanliness
5/1x0.025; L1x0.004

Coating specifications front side  (S2)

(113621)
[  ~  ]
List all articles with the same coating as the current front side coating

Coating specifications rear side  (S1)

(120998)
[  ~  ]
List all articles with the same coating as the current rear side coating
1st operating range   HRu(0-10°,1030-1360nm)>99.8%
Type
High Reflectance
Polarisation
unpol.
unpolarized  =  s + p2
Angle of incidence
0 - 10°
Wavelength range
1030 - 1360 nm
HR
> 99.8 %
2nd operating range   Ru(0-10°,530-630nm)<5%
Type
Polarisation
unpol.
unpolarized  =  s + p2
Angle of incidence
0 - 10°
Wavelength range
530 - 630 nm
AR / HT
< 5 %
1st operating range   ARu(0-10°,500-700nm)<0.8%
Type
Anti-Reflectance
Polarisation
unpol.
unpolarized  =  s + p2
Angle of incidence
0 - 10°
Wavelength range
500 - 700 nm
AR / HT
< 0.8 %