Separator:
Fused silica | plane | Ø=12.7(-0.1)mm | t=6.35(±0.10)mm | wedge=30min
S1: wedge side | Øe10 | 3/0.2(0.2) [L/10] | 5/1x0.025; L1x0.004 |
chamfer 1.0
     ARu(45°,700-1100nm)<1%
S2(^): Øe10 | 3/0.2(0.2) [L/10] | 5/1x0.025; L1x0.004 | chamfer 1.0
     HRs(45°,470-570nm)>99.9% + Rs,p(45°,700-1100nm)<5%
     |GDD-Rs(45°,490-570nm)|<20fs²

Product

plane+plane
Round
Article
101940
Type
  • Separator
  • Combiner
Laser type
  • Ti:Sa Laser
  • Yb:YAG-Laser
  • Nd:YAG-Laser
Price per unit (net.)
$174.93
discount ▼
from 5 pieces
5 %
from 10 pieces
10 %
from 20 pieces
20 %
Stock
0

General Optical Parameters

Material
Fused Silica
Shape
Round
Diameter (Ø)
12.7 mm
(-0.1  mm)
Thickness (t)
6.35 mm
(±0.1 mm)

Optical Parameters Front Side  (S2)

Optical Parameters Rear Side  (S1)

Shape
plane
Chamfer
0.3 mm
(±0.1 mm)
Test area Øe
10
Surface form tolerance
3/0.2(0.2) [L/10 @546.1nm]
Cleanliness
5/1x0.025; L1x0.004
Shape
plane
Wedge
30ʹ
Chamfer
1 mm
(±0.1 mm)
Test area Øe
10
Surface form tolerance
3/0.2(0.2) [L/10 @546.1nm]
Cleanliness
5/1x0.025; L1x0.004

Coating specifications front side  (S2)

[  ~  ]
List all articles with the same coating as the current front side coating

Coating specifications rear side  (S1)

[  ~  ]
List all articles with the same coating as the current rear side coating
1st operating range   HRs(45°,470-570nm)>99.9%
Type
High Reflectance
Polarisation
s-Pol.
Angle of incidence
45°
Wavelength range
470 - 570 nm
HR
> 99.9 %
2nd operating range   Ru(45°,700-1100nm)<5%
Type
Polarisation
unpol.
unpolarized  =  s + p2
Angle of incidence
45°
Wavelength range
700 - 1100 nm
AR / HT
< 5 %
3rd operating range   |GDDs(45°,490-570nm)|<20fs²
Type
Group Delay Dispersion
Polarisation
s-Pol.
Angle of incidence
45°
Wavelength range
490 - 570 nm
GDD
0 fs²
(±20 fs²)
1st operating range   ARu(45°,600-1100nm)<1%
Type
Anti-Reflectance
Polarisation
unpol.
unpolarized  =  s + p2
Angle of incidence
45°
Wavelength range
600 - 1100 nm
AR / HT
< 1 %