Datasheet - Laser mirror 102103

[  ~  ]
List all articles with the similar coating
Print
Laser Mirror:
Fused silica | pl-concave | Ø=25.0(-0.1)mm | te=6.35(±0.1)mm | //<5min
S1: Øe21 | 3/0.2(0.2) [L/10] | 5/2x0.04; L1x0.004 | chamfer 0.3
     AR(0°,1520-1670nm)<0.25%
S2(^): r=1000mm(±1%) CC | Øe21 | 3/-(0.2) [L/10 reg.] | 5/1x0.04;
L1x0.004 | chamfer 0.3
     Øe10 | 5/1x0.016
     HR(0°,1520-1670nm)>99.99% (Low Loss)
     T(0°,1600nm)~0.001%

Product

concave+plane
Round
Article
102103
Type
  • Laser mirror
Laser category
  • Low Loss Optics
Coating material (front side)
134129
Coating material (rear side)
131781
Price per unit (net.)
on request
discount ▼
from 5 pieces
5 %
from 10 pieces
10 %
from 20 pieces
20 %
Stock
0

General Optical Parameters

Material
Corning 7980 2F or equal
Shape
Round
Diameter (Ø)
25 mm
(-0.1 mm)
Thickness (t)
6.35 mm
(±0.1 mm)
Parallelism

Optical Parameters Front Side  (S2)

Optical Parameters Rear Side  (S1)

Shape
concave
Radius of curvature
1,000 mm
(±1 %)
Chamfer
0.3 mm
(±0.1 mm)
Test area Øe
21
Surface form tolerance
3/-(0.2) [L/10 reg. @546.1nm]
Cleanliness
5/1x0.04; L1x0.004
Inner test area Øe
10
Cleanliness
5/1x0.016
Shape
plane
Chamfer
0.3 mm
(±0.1 mm)
Test area Øe
21
Surface form tolerance
3/0.2(0.2) [L/10 @546.1nm]
Cleanliness
5/2x0.04; L1x0.004

Coating specifications front side  (S2)

(134129)
[  ~  ]
List all articles with the same coating as the current front side coating

Coating specifications rear side  (S1)

(131781)
[  ~  ]
List all articles with the same coating as the current rear side coating
1st operating range   HR(0°,1520-1670nm)>99.99%
Type
High Reflectance
Polarisation
unpol.
unpolarized  =  s + p2
Angle of incidence
Wavelength range
1520 - 1670 nm
HR
> 99.99 %
2nd operating range   T(0°,1520-1670nm)~0.001%
Type
Transmittance
Polarisation
unpol.
unpolarized  =  s + p2
Angle of incidence
Wavelength range
1520 - 1670 nm
T
~ 0.001 %
1st operating range   AR(0°,1520-1670nm)<0.25%
Type
Anti-Reflectance
Angle of incidence
Wavelength range
1520 - 1670 nm
AR / HT
< 0.25 %