Datasheet - Short Wave Pass Filter 104634

[  ~  ]
List all articles with the similar coating
Print
Short Wave Pass Filter:
Fused silica | pl-concave | Ø=25.0(-0.1)mm | te=6.35(±0.10)mm | //<5min
S1: Øe21 | 3/0.2(0.2) [L/10] | 5/3x0.04; L1x0.004 | chamfer 0.3
     AR(0°,800-1000nm)<0.2%
S2(^): r=100mm(±0.5%) CC | Øe21 | 3/-(0.2) [L/10 reg.] | 5/3x0.04;
L1x0.004 | chamfer 0.3
     HR(0°,1030-1200nm)>99.9% + R(0°,820-990nm)<2%

Product

concave+plane
Round
Article
104634
Type
  • Short Wave Pass Filter
Laser category
  • cw-Laser Optics
  • ns-Laser Optics
Laser type
  • Yb:YAG-Laser
  • Nd:YAG-Laser
Coating material (front side)
128040
Coating material (rear side)
115720
Price per unit (net.)
$718.87
discount ▼
from 5 pieces
5 %
from 10 pieces
10 %
from 20 pieces
20 %
Stock
2

General Optical Parameters

Material
Corning 7980 2F or equal
Shape
Round
Diameter (Ø)
25 mm
(-0.1 mm)
Thickness (t)
6.35 mm
(±0.1 mm)
Edge thickness
6.35 mm
Parallelism

Optical Parameters Front Side  (S2)

Optical Parameters Rear Side  (S1)

Shape
concave
Radius of curvature
100 mm
(±0.5 %)
Chamfer
0.3 mm
(±0.1 mm)
Test area Øe
21
Surface form tolerance
3/-(0.2) [L/10 reg. @546.1nm]
Cleanliness
5/3x0.04; L1x0.004
Shape
plane
Chamfer
0.3 mm
(±0.1 mm)
Test area Øe
21
Surface form tolerance
3/0.2(0.2) [L/10 @546.1nm]
Cleanliness
5/3x0.04; L1x0.004

Coating specifications front side  (S2)

(128040)
[  ~  ]
List all articles with the same coating as the current front side coating

Coating specifications rear side  (S1)

(115720)
[  ~  ]
List all articles with the same coating as the current rear side coating
1st operating range   HR(0°,1030-1200nm)>99.9%
Type
High Reflectance
Polarisation
unpol.
unpolarized  =  s + p2
Angle of incidence
Wavelength range
1030 - 1200 nm
HR
> 99.9 %
2nd operating range   R(0°,820-990nm)<2%
Type
Angle of incidence
Wavelength range
820 - 990 nm
R
< 2 %
1st operating range   AR(0°,800-1000nm)<0.2%
Type
Anti-Reflectance
Polarisation
unpol.
unpolarized  =  s + p2
Angle of incidence
Wavelength range
800 - 1000 nm
AR / HT
< 0.2 %