Datasheet - Pump Mirror 105914

[  ~  ]
List all articles with the similar coating
Print
Pump Mirror:
Fused silica | pl-concave | Ø=12.7(-0.1)mm | te=6.35(±0.10)mm | //<5min
S1: Øe10 | 3/0.2(0.2) [L/10] | 5/1x0.025; L1x0.004 | chamfer 0.3
     AR(0°, 390-440nm)<0.25%
S2(^): r=60mm(±0.5%) CC | Øe10 | 3/-(0.5) [L/4 reg.] | 5/1x0.025;
L1x0.004 | chamfer 0.3
     HR(0°,(780-900)±8nm)>99.9% + R(0°,(390-420)±4nm)<3%
     |GDD-R(0°,(790-890)±8nm)|<20fs²

Product

concave+plane
Round
Article
105914
Type
  • Pump Mirror
Laser category
  • fs-Laser Optics
Laser type
  • Ti:Sa Laser
Coating material (front side)
114398
Coating material (rear side)
123415
Price per unit (net.)
€157.00
discount ▼
from 5 pieces
5 %
from 10 pieces
10 %
from 20 pieces
20 %
Stock
3

General Optical Parameters

Material
Fused Silica
Shape
Round
Diameter (Ø)
12.7 mm
(-0.1  mm)
Thickness (t)
6.35 mm
(±0.1 mm)
Parallelism

Optical Parameters Front Side  (S2)

Optical Parameters Rear Side  (S1)

Shape
concave
Radius of curvature
60 mm
(±0.5 %)
Chamfer
0.3 mm
(±0.1 mm)
Test area Øe
10
Surface form tolerance
3/-(0.5) [L/4 reg. @546nm]
Cleanliness
5/1x0.025; L1x0.004
Shape
plane
Chamfer
0.3 mm
(±0.1 mm)
Test area Øe
10
Surface form tolerance
3/0.2(0.2) [L/10 @546nm]
Cleanliness
5/1x0.025; L1x0.004

Coating specifications front side  (S2)

(114398)
[  ~  ]
List all articles with the same coating as the current front side coating

Coating specifications rear side  (S1)

(123415)
[  ~  ]
List all articles with the same coating as the current rear side coating
1st operating range   HR(0°,780-900nm)>99.9%, |GDD|<20fs²
Type
High Reflectance
Polarisation
unpol.
unpolarized  =  s + p2
Angle of incidence
Wavelength range
780 - 900 nm
HR
> 99.9 %
GDD
0 fs²
(±20 fs²)
2nd operating range   R(0°,390-420nm)<3%
Type
Polarisation
unpol.
unpolarized  =  s + p2
Angle of incidence
Wavelength range
390 - 420 nm
AR / HT
< 3 %
1st operating range   AR(0°,380-430nm)<0.25%
Type
Anti-Reflectance
Polarisation
unpol.
unpolarized  =  s + p2
Angle of incidence
Wavelength range
380 - 430 nm
AR / HT
< 0.25 %